This fiberglass fabric is a fabric woven in plain or twill method with E-glass roving. The plain or twill weave pattern ensures a smooth and even surface, making it ideal for projects that require a sleek finish. The fabric could be easily impregnated with resin and it comes out with high adhesive strength.
Our fabric is specially treated with s ilane, enhancing its resistance to moisture and improving its overall performance. This treatment also enhances the fabric's adhesion to resins, making it an excellent choice for composite application
Whether you need fiberglass cloth for automotive repairs, boat building, or industrial applications, our Fiberglass Fabric is the perfect solution. Trust in its quality and versatility to deliver outstanding results every time.
Characteristics:
Item | Weight (g/m2) | Thickness (mm) | Filament (um) | Density (/cm) | Tensile strength (N/25mm) | Weave | Moisture Content (%) | Loss Ignition (%) | Agent type | ||
Warp | Weft | Warp | Weft | ||||||||
JLP30 | 30 | 0.03 | 4.5 | 8 | 4 | 160 | 70 | Plain | 1.00 | 0.6-1.0 | Silane |
JLP60 | 60 | 0.06 | 5.5 | 12.5 | 12.5 | 260 | 260 | Plain | 1.00 | 0.6-1.0 | Silane |
JLP80 | 80 | 0.08 | 9 | 33 | 33 | 300 | 300 | Plain | 1.00 | 0.6-1.0 | Silane |
JLT80 | 80 | 0.08 | 9 | 33 | 33 | 300 | 300 | Twill | 1.00 | 0.6-1.0 | Silane |
Surface veil for FRP laminates
Model building, RC aircraft, drones, and hobby composites
Surfboard and paddle board finishing layers
Transparent protective top layers
Composite repair and micro-reinforcement
Speaker cones, tubes, and thin-walled composite parts
Waterproofing layers for wood, foam, and laminates
Electrical and electronic insulation layers
Extremely lightweight while maintaining structural contribution
Creates a very smooth outer surface
Reduces print-through of heavier fabrics
Provides uniform resin absorption and clarity
Suitable for professional and DIY composite projects
Enhances surface strength without significant weight increase
This fiberglass fabric is a fabric woven in plain or twill method with E-glass roving. The plain or twill weave pattern ensures a smooth and even surface, making it ideal for projects that require a sleek finish. The fabric could be easily impregnated with resin and it comes out with high adhesive strength.
Our fabric is specially treated with s ilane, enhancing its resistance to moisture and improving its overall performance. This treatment also enhances the fabric's adhesion to resins, making it an excellent choice for composite application
Whether you need fiberglass cloth for automotive repairs, boat building, or industrial applications, our Fiberglass Fabric is the perfect solution. Trust in its quality and versatility to deliver outstanding results every time.
Characteristics:
Item | Weight (g/m2) | Thickness (mm) | Filament (um) | Density (/cm) | Tensile strength (N/25mm) | Weave | Moisture Content (%) | Loss Ignition (%) | Agent type | ||
Warp | Weft | Warp | Weft | ||||||||
JLP30 | 30 | 0.03 | 4.5 | 8 | 4 | 160 | 70 | Plain | 1.00 | 0.6-1.0 | Silane |
JLP60 | 60 | 0.06 | 5.5 | 12.5 | 12.5 | 260 | 260 | Plain | 1.00 | 0.6-1.0 | Silane |
JLP80 | 80 | 0.08 | 9 | 33 | 33 | 300 | 300 | Plain | 1.00 | 0.6-1.0 | Silane |
JLT80 | 80 | 0.08 | 9 | 33 | 33 | 300 | 300 | Twill | 1.00 | 0.6-1.0 | Silane |
Surface veil for FRP laminates
Model building, RC aircraft, drones, and hobby composites
Surfboard and paddle board finishing layers
Transparent protective top layers
Composite repair and micro-reinforcement
Speaker cones, tubes, and thin-walled composite parts
Waterproofing layers for wood, foam, and laminates
Electrical and electronic insulation layers
Extremely lightweight while maintaining structural contribution
Creates a very smooth outer surface
Reduces print-through of heavier fabrics
Provides uniform resin absorption and clarity
Suitable for professional and DIY composite projects
Enhances surface strength without significant weight increase