| PRODUCT ITEM | 3*3*M45 | ||
| WARP YARN | 68 TEX | ||
| WEFT YARN | 68 TEX | ||
| WARP TENSILE | N/50mm | 820 | |
| WEFT TENSILE | N/50mm | 820 | |
| WATER CONTENT | % | 0.16 | |
| THICKNESS | mm | 0.45 | |
| MATERIAL WEIGHT | g/m² | 120±8% | |
| ADHESIVE | PVOH | ||
JLON designs and manufactures biaxial and multi-axial laid scrim based on client specifications. Our raw materials include fiberglass, polyester and other synthetic fibers. Relying on technology patents, our R&D team strives to provide innovative solutions using the most advanced material and technology available.
Nonwoven laid scrim is manufactured by laying continuous filament yarn in biaxial or multiaxial directions and bonding by adhesive to hold structure and stability of the scrim. Due to open construction, laid scrim is the most effective and economic solution for flexible reinforcements. A layer of glass or polyester veil can be laminated to scrim.
Laid Scrim can increase strength, stabilize structure with high strength and light weight. It can be fully bonded with almost any material.
Dimensional stability
Tensile strength
Tear resistance
Fiberglass
Polyester
Polyvinyl alcohol
Acrylic
PVC
Hot melt
Biaxial
Triaxial
JLON glass laid scrim is made of continous glass fiber yarns.
Yarn | Mesh size (mm) | Area weight (g/m2) | Min.tensile strength（N） | Angle/ Binder | ||
Warp | Weft | |||||
001G | 34tex | 5*5 | 15.5±8% | 200 | 200 | |
002G | 34tex | 10*10 | 7.78±8% | 100 | 100 | |
003G | 34tex | 3*3 | 25±8% | 280 | 280 | |
004G | 34tex | 6.25*6.25 | 12.4±8% | 150 | 150 | |
005G | 34tex | 6.25*12.5 | 9.3±8% | 150 | 70 | |
006G | 34tex | 12.5*12.5 | 6.3±8% | 80 | 80 | |
007G | 68tex | 5*5 | 31.68±8% | 350 | 350 | |
008G | 68tex | 8*8 | 20±8% | 250 | 250 | |
009G | 22.5tex | 5*10 | 7.9±8% | 150 | 80 | |
010G | 34tex*68tex | 2.5+10*8 | 16±8% | 100 | 180 | |
011G | 68tex | 2.5+10*8 | 22±8% | 400 | 320 | |
012G | 34tex | 3*12 | 16±8% | 300 | 80 | |
013G | 68tex | 3*10 | 33±8% | 360 | 200 | |
015G | 68tex*34tex | 5*5 | 24±8% | 350 | 180 | |
016G | 68tex | 12.5*12.5 | 12.5±8% | 160 | 160 | |
017G | 34tex | 5*10 | 12.2±8% | 200 | 100 | |
018G | 68tex | 6.25*6.25 | 24.6±8% | 250 | 250 | |
001LG | 68tex*136tex | 3*8*8 | 60±8% | 600 | 400 | ±75° |
002LG | 34tex | 5*5*5 | 25±8% | 200 | 200 | ±75° |
JLON polyester laid scrim is made of polyester continous yarns.
Product Code | Yarn | Mesh Size (mm) | Area Weight (g/m2) | Min. Tensile Strength (N) | Angle/Binder | ||
Warp | Weft | ||||||
001F | 83dtex*2*167dtex | 4*6.5 | 9.6±8% | 75 | 45 | ||
002F | 83dtex*2*83dtex | 5*5 | 8.8±8% | 50 | 25 | ||
003F | 83dtex | 2.5*5 | 6.5±8% | 70 | 25 | ||
004F | 83dtex | 2.5*10 | 6.2±8% | 70 | 15 | ||
005F | 83dtex | 5*10 | 4.7±8% | 25 | 15 | ||
006F | 110dtex | 8*12.5 | 4.7±8% | 20 | 15 | Hot melt | |
007F | 83dtex | 6.25*8 | 4.3±8% | 25 | 20 | ||
008F | 83dtex | 6.25*12.5 | 3±8% | 25 | 15 | ||
009F | 83dtex | 12.5*12.5 | 1.7±8% | 15 | 15 | ||
010F | 110dtex | 10*10 | 4.3±8% | 15 | 15 | Hot melt | |
011F | 550dtex | 4*4 | 38.5±8% | 350 | 350 | ||
012F | 83dtex*2*167dtex | 3*10 | 9.8±8% | 70 | 30 | ||
016F | 1100dtex | 10*10 | 30.8±8% | 300 | 300 | ||
017F | 550dtex | 5*5 | 30±8% | 300 | 300 | ||
018F | 550dtex*1100dtex | 5*5 | 41±8% | 300 | 500 | ||
019F | 83dtex | 2*5 | 9±8% | 75 | 25 | ||
020F | 1100dtex | 5*5 | 58±8% | 400 | 400 | ||
021F | 2200dtex*550dtex | 4*6 | 75±8% | 1000 | 250 | ||
022F | 167dtex | 12.5*12.5 | 4±8% | 25 | 25 | ||
024F | 1100dtex | 4*4 | 68.2±8% | 500 | 500 | ||
025F | 550dtex | 5*5 | 45.8±8% | 300 | 300 | PVC胶 | |
026F | （550dtex*3+3300dtex）* （550dtex*3+2200dtex*2） | 2.5*5 | 97±8% | 1000 | 600 | 防水胶 | |
027F | （550dtex*4+2200dtex）* （550dtex*4+1100dtex） | 3*5 | 62±8% | 450 | 180 | 防水胶 | |
028F | 2200dtex*550dtex | 4*5 | 86±8% | 1000 | 300 | 防水胶 | |
029F | （550dtex*5+2200dtex） *550dtex | 5*5 | 46±8% | 250 | 130 | 防水胶 | |
030F | 2200dtex*550dtex | 4*6.25 | 83±8% | 1000 | 130 | 防水胶 | |
031F | 1670dtex*550dtex | 4*6.25 | 66±8% | 700 | 130 | 防水胶 | |
032F | 1100dtex*550dtex | 4*6.25 | 47±8% | 500 | 130 | 防水胶 | |
033F | 83dtex | 4*6.25 | 5±8% | 30 | 15 | ||
034F | 167dtex | 15*15 | 3±8% | 20 | 20 | ||
035F | 83dtex*2*167dtex | 3*7 | 10.5±8% | 80 | 45 | ||
037F | 83dtex | 10*10 | 2.9±8% | 15 | 15 | ||
001LF | 1100dtex | 9*16*16 | 31.6±8% | 300 | 150 | ±75° | |
003LF | 1100dtex | 35*12.5*12.5 | 27.5±8% | 80 | 150 | ±75° | |
004LF | 83dtex | 3*25*25 | 4.3±8% | 50 | 10 | ±75° | |
Laid scrim could be laminated with a layer of glass fiber or polyester veil. It protects the reinforced materials from expanding or shrinking with the variations in temperature and humidity and also help with installation.
Code | Yarn | Mesh Size (mm) | Laminate | Area Weight (g/m2) | Tensile Strength (N/5cm) | Binder |
JL70G35 | 34tex | 3x5mm | 35gsm glass | 70 | Warp:350 Weft: 200 | PVC |
JL60F25 | 68tex | 4x6.5mm | 25gsm nonwoven | 60 | Warp: 600 Weft: 350 | PVC & acrylic |
JL60G35 | 34tex | 3x10mm | 35gsm glass | 60 | Warp:300 Weft: 100 | PVC |
JL100G35 | 68tex | 3x3mm | 35gsm glass | 100 | Warp: 700 Weft: 700 | PVC |
JL130F25 | 68tex | 3x3mm | 25gsm nonwoven | 130 | Warp: 900 Weft: 500 | PVC |
JL90F30 | 68tex | 3x3mm | 30gsm nonwoven | 90 | Warp: 1000 Weft: 1000 | Acrylic |
JL190F105 | 68tex | 3x3mm | 105gsm nonwoven combi | 190 | Warp: 1200 Weft: 800 | Acrylic |
JL130F35 | 136tex | 3x3mm | 35gsm nonwoven | 130 | Warp: 1500 Weft: 1600 | PVC & acrylic |
JL230G35 | 200tex | 3x3mm | 35gsm glass | 230 | Warp: 1900 Weft: 2200 | PVC & acrylic |
JL280G70 | 200tex | 3x3mm | 70gsm glass | 280 | Warp: 2000 Weft: 2500 | PVC |
JL160G50 | 136tex | 4x4mm | 50gsm glass | 160 | Warp: 1100 Weft: 1200 | PVC |
| PRODUCT ITEM | 3*3*M45 | ||
| WARP YARN | 68 TEX | ||
| WEFT YARN | 68 TEX | ||
| WARP TENSILE | N/50mm | 820 | |
| WEFT TENSILE | N/50mm | 820 | |
| WATER CONTENT | % | 0.16 | |
| THICKNESS | mm | 0.45 | |
| MATERIAL WEIGHT | g/m² | 120±8% | |
| ADHESIVE | PVOH | ||
JLON designs and manufactures biaxial and multi-axial laid scrim based on client specifications. Our raw materials include fiberglass, polyester and other synthetic fibers. Relying on technology patents, our R&D team strives to provide innovative solutions using the most advanced material and technology available.
Nonwoven laid scrim is manufactured by laying continuous filament yarn in biaxial or multiaxial directions and bonding by adhesive to hold structure and stability of the scrim. Due to open construction, laid scrim is the most effective and economic solution for flexible reinforcements. A layer of glass or polyester veil can be laminated to scrim.
Laid Scrim can increase strength, stabilize structure with high strength and light weight. It can be fully bonded with almost any material.
Dimensional stability
Tensile strength
Tear resistance
Fiberglass
Polyester
Polyvinyl alcohol
Acrylic
PVC
Hot melt
Biaxial
Triaxial
JLON glass laid scrim is made of continous glass fiber yarns.
Yarn | Mesh size (mm) | Area weight (g/m2) | Min.tensile strength（N） | Angle/ Binder | ||
Warp | Weft | |||||
001G | 34tex | 5*5 | 15.5±8% | 200 | 200 | |
002G | 34tex | 10*10 | 7.78±8% | 100 | 100 | |
003G | 34tex | 3*3 | 25±8% | 280 | 280 | |
004G | 34tex | 6.25*6.25 | 12.4±8% | 150 | 150 | |
005G | 34tex | 6.25*12.5 | 9.3±8% | 150 | 70 | |
006G | 34tex | 12.5*12.5 | 6.3±8% | 80 | 80 | |
007G | 68tex | 5*5 | 31.68±8% | 350 | 350 | |
008G | 68tex | 8*8 | 20±8% | 250 | 250 | |
009G | 22.5tex | 5*10 | 7.9±8% | 150 | 80 | |
010G | 34tex*68tex | 2.5+10*8 | 16±8% | 100 | 180 | |
011G | 68tex | 2.5+10*8 | 22±8% | 400 | 320 | |
012G | 34tex | 3*12 | 16±8% | 300 | 80 | |
013G | 68tex | 3*10 | 33±8% | 360 | 200 | |
015G | 68tex*34tex | 5*5 | 24±8% | 350 | 180 | |
016G | 68tex | 12.5*12.5 | 12.5±8% | 160 | 160 | |
017G | 34tex | 5*10 | 12.2±8% | 200 | 100 | |
018G | 68tex | 6.25*6.25 | 24.6±8% | 250 | 250 | |
001LG | 68tex*136tex | 3*8*8 | 60±8% | 600 | 400 | ±75° |
002LG | 34tex | 5*5*5 | 25±8% | 200 | 200 | ±75° |
JLON polyester laid scrim is made of polyester continous yarns.
Product Code | Yarn | Mesh Size (mm) | Area Weight (g/m2) | Min. Tensile Strength (N) | Angle/Binder | ||
Warp | Weft | ||||||
001F | 83dtex*2*167dtex | 4*6.5 | 9.6±8% | 75 | 45 | ||
002F | 83dtex*2*83dtex | 5*5 | 8.8±8% | 50 | 25 | ||
003F | 83dtex | 2.5*5 | 6.5±8% | 70 | 25 | ||
004F | 83dtex | 2.5*10 | 6.2±8% | 70 | 15 | ||
005F | 83dtex | 5*10 | 4.7±8% | 25 | 15 | ||
006F | 110dtex | 8*12.5 | 4.7±8% | 20 | 15 | Hot melt | |
007F | 83dtex | 6.25*8 | 4.3±8% | 25 | 20 | ||
008F | 83dtex | 6.25*12.5 | 3±8% | 25 | 15 | ||
009F | 83dtex | 12.5*12.5 | 1.7±8% | 15 | 15 | ||
010F | 110dtex | 10*10 | 4.3±8% | 15 | 15 | Hot melt | |
011F | 550dtex | 4*4 | 38.5±8% | 350 | 350 | ||
012F | 83dtex*2*167dtex | 3*10 | 9.8±8% | 70 | 30 | ||
016F | 1100dtex | 10*10 | 30.8±8% | 300 | 300 | ||
017F | 550dtex | 5*5 | 30±8% | 300 | 300 | ||
018F | 550dtex*1100dtex | 5*5 | 41±8% | 300 | 500 | ||
019F | 83dtex | 2*5 | 9±8% | 75 | 25 | ||
020F | 1100dtex | 5*5 | 58±8% | 400 | 400 | ||
021F | 2200dtex*550dtex | 4*6 | 75±8% | 1000 | 250 | ||
022F | 167dtex | 12.5*12.5 | 4±8% | 25 | 25 | ||
024F | 1100dtex | 4*4 | 68.2±8% | 500 | 500 | ||
025F | 550dtex | 5*5 | 45.8±8% | 300 | 300 | PVC胶 | |
026F | （550dtex*3+3300dtex）* （550dtex*3+2200dtex*2） | 2.5*5 | 97±8% | 1000 | 600 | 防水胶 | |
027F | （550dtex*4+2200dtex）* （550dtex*4+1100dtex） | 3*5 | 62±8% | 450 | 180 | 防水胶 | |
028F | 2200dtex*550dtex | 4*5 | 86±8% | 1000 | 300 | 防水胶 | |
029F | （550dtex*5+2200dtex） *550dtex | 5*5 | 46±8% | 250 | 130 | 防水胶 | |
030F | 2200dtex*550dtex | 4*6.25 | 83±8% | 1000 | 130 | 防水胶 | |
031F | 1670dtex*550dtex | 4*6.25 | 66±8% | 700 | 130 | 防水胶 | |
032F | 1100dtex*550dtex | 4*6.25 | 47±8% | 500 | 130 | 防水胶 | |
033F | 83dtex | 4*6.25 | 5±8% | 30 | 15 | ||
034F | 167dtex | 15*15 | 3±8% | 20 | 20 | ||
035F | 83dtex*2*167dtex | 3*7 | 10.5±8% | 80 | 45 | ||
037F | 83dtex | 10*10 | 2.9±8% | 15 | 15 | ||
001LF | 1100dtex | 9*16*16 | 31.6±8% | 300 | 150 | ±75° | |
003LF | 1100dtex | 35*12.5*12.5 | 27.5±8% | 80 | 150 | ±75° | |
004LF | 83dtex | 3*25*25 | 4.3±8% | 50 | 10 | ±75° | |
Laid scrim could be laminated with a layer of glass fiber or polyester veil. It protects the reinforced materials from expanding or shrinking with the variations in temperature and humidity and also help with installation.
Code | Yarn | Mesh Size (mm) | Laminate | Area Weight (g/m2) | Tensile Strength (N/5cm) | Binder |
JL70G35 | 34tex | 3x5mm | 35gsm glass | 70 | Warp:350 Weft: 200 | PVC |
JL60F25 | 68tex | 4x6.5mm | 25gsm nonwoven | 60 | Warp: 600 Weft: 350 | PVC & acrylic |
JL60G35 | 34tex | 3x10mm | 35gsm glass | 60 | Warp:300 Weft: 100 | PVC |
JL100G35 | 68tex | 3x3mm | 35gsm glass | 100 | Warp: 700 Weft: 700 | PVC |
JL130F25 | 68tex | 3x3mm | 25gsm nonwoven | 130 | Warp: 900 Weft: 500 | PVC |
JL90F30 | 68tex | 3x3mm | 30gsm nonwoven | 90 | Warp: 1000 Weft: 1000 | Acrylic |
JL190F105 | 68tex | 3x3mm | 105gsm nonwoven combi | 190 | Warp: 1200 Weft: 800 | Acrylic |
JL130F35 | 136tex | 3x3mm | 35gsm nonwoven | 130 | Warp: 1500 Weft: 1600 | PVC & acrylic |
JL230G35 | 200tex | 3x3mm | 35gsm glass | 230 | Warp: 1900 Weft: 2200 | PVC & acrylic |
JL280G70 | 200tex | 3x3mm | 70gsm glass | 280 | Warp: 2000 Weft: 2500 | PVC |
JL160G50 | 136tex | 4x4mm | 50gsm glass | 160 | Warp: 1100 Weft: 1200 | PVC |