| Name | Type | 25℃aPa.s Viscosity | 25℃min Gel Time | %Non-volatile | MPa Tensile Strength | %Elongation | MPa Flexural Strength | ℃distortion Temperature | Application&Remarks | Hand lay-up general purpose resin |
| JL-189 | 0.25-0.45 | 10.5-21.5 | 60-66 | 61 | 4.6 | 110 | 62 | Hand lay-up general purpose resin, marine,high damage elongation,water resistance,CCS certification | ||
| JL-191 | 0.25-0.45 | 9.0-17.0 | 61-67 | 64 | 3.6 | 112 | 66 | General hand lay-up,winding,higher elongation | ||
| JL-1032 | 0.34-0.42 | 10.0-30.0 | / | 62 | 2.0 | 118 | 69 | Finshing boat,yacht,hand lay-up, spray up,low shrinkage,water resistance,CCS certification | Hand lay-up,spray up promote thixotropic resin | |
| JL-10070TP | 0.4-0.6 | 10.0-50.0 | / | 58 | 2.0 | 100 | 86 | S/F and F/F double wall tanks,UI1316/1746/1856 certified | ||
| JL-3002 | 0.14-0.18 | 20.0-100.0 | 56.0-62.0 | 270 | / | 300 | / | Vacuum infusion process,RTM process,low viscosity,good fiberglass wettability | Flame retardant resin(data for FRP) | |
| JL-107BH | 0.40-0.50 | 16.0-25.0 | 56.0-62.0 | 300 | / | 325 | / | Good flame retardant property,high mechanical strength,used for ships,vechicles,construction,etc | ||
| JL-T1 | 0.35-0.55 | 7.0-12.0 | 60.0-66.0 | 71 | 3.2 | 110 | 112 | Used for corrosion resistant,high strength pultrusion products,high strength,good heat resistance | Pultrusion resin | |
| JL-611H | 0.50-0.80 | 10.0-18.0 | 64.0-70.0 | 62 | 3.0 | 110 | 60 | General purpose pultrusion resin,high viscosity,good surface gloss | ||
| JL-21 | 0.14-0.18 | 20.0-110.0 | 53.0-59.0 | 60 | 2 | 108 | 65 | Used for fishing boats and yachts,pre-promotion,low reactivity,shrinkage | RTM/Vacuum infusion | |
| JL-25 | 0.14-0.18 | 20.0-110.0 | 53.0-59.0 | 71 | 3.8 | 122 | 75 | Pre-promotion,low heat release,good toughness,CCS certification | ||
| JL-102 | 0.20-0.40 | 7.0-13.0 | 58.0-64.0 | 65 | 2.8 | 120 | 103 | Used for temperature resistance FRP pipe,tank structure layer,corrosion resistance,high thermal deformation temperature | Winding resin | |
| JL-192 | 0.30-0.50 | 18.0-28.0 | 62.0-68.0 | 75 | 3.3 | 120 | 92 | High reactivity,high strength and structural layer | ||
| JL-D31 | 0.30-0.60 | 8.0-16.0 | 58.0-64.0 | 60 | 2.8 | 122 | 90 | Good toughness and strength,suitable for water-resistant gelcoat matrix | Gelcoat matrix resin | |
| JL-D34 | 0.65-1.15 | 8.0-18.0 | 64.0-70.0 | 76 | 2.6 | 128 | 73 | Good toughness and strength,used for toughness general purpose gelcoat matrix | ||
| JL-1017 | 0.50-0.80 | 16.0-24.0 | 62.0-68.0 | 75 | 2.0 | 100 | 70 | Good mechanical properties,good cracking resistance,fast demoulding,used for concrete castling | Casting resin | |
| JL-2250 | 0.13-0.18 | 8.0-14.0 | 66.0-70 | 40 | 1.0 | 60 | 80 | Low shrinkage,low viscosity,high filling rate,used for polyester concrete | ||
| JL-2 | 0.60-0.80 | 8.0-14.0 | 58.5-64.5 | 50 | 1.6 | 83 | 123 | High gloss,water resistance,heat resistance,good electrical properties,SMC/BMC resin | S/BMC molded resin and low shrinkage agent | |
| JL-6 | 1.10-1.50 | 8.0-11.0 | 63.0-69.0 | 62 | 2.4 | 105 | 110 | High reactivity,good thickening,smooth surface,SMC/BMC resin |
JL-1032 is a kind of water resistance resin, viscosity moderation, good mechanical strength. It can be applied in FRP products of motor shell and boats parts as well as lay-up products. It passed CCS approval.
| Item | Unit | Index | Test standard |
| Appearance | -- | Transparent,light yellow | GB/T 8237.4.1.1 |
| Viscosity | 25ºC,Pa.S | 0.25~0.45 | GB/T 7193.1 |
| Gel time | 25ºC,min | 10.5~21.5 | GB/T 7193.6 |
| Acid value | mgKOH/g | 19~27 | GB/T 2895 |
| Non-volatile | % | 59~65 | GB/T 7193.3 |
Gel Time: 50% cyclohexanon peroxide: 4%; Accelerator E1: 4% :
| item | Unit | Measured value | Test standard |
| Barcol Hardness | -- | 46 | GB 3854-83 |
| HDT | ºC | 57 | GB 1634-04 |
| Elongation at break | % | 4.0 | GB/T 2568-95 |
| water absorption | % | 0.1 | GB/T 1462-88 |
Remark : casting matrix should follow GB8237-87
Hardness system : hardener 55%MEKPO :2% ; accelerator E1 :2%
Later Hardness system :60 ºC×2 hours + 80 ºC×2 hours
The loading and transportation must follow the rules in chapter 5 of dangerous chemicals regulations .The products should stored under 25 ºC and avoid the sunshine ,heat source and fire source. The shelf life is 6 month.
JL-10070TP is a medium viscosity orthophthalic unsaturated polyester resin, pre-accelerated, thixotropic, with wax. Extending its FRP products has good mechanical strength and high elongation rate, suitable for general purpose hand lay up FRP products.
JL-10070TP unsaturated polyester resin is a pre-promoted, thixotropic general purpose resin. It has low viscosity, good infiltration to glass fibre, and excellent thixotropic construction.
JL-10070TP unsaturated polyester resin is a pre-promoted, thixotropic general-purpose resin with low viscosity. It is suitable for hand lay-up or injection moulding of various FRP products, such as FRP cooling towers, vehicle shells and other FRP moulded products.
FRP cooling towers, vehicle shells and other FRP moulded products. JL-10070TP contains wax, JL-10070TPN does not contain wax.
| Item | unit | Indicators | Test Methods |
| Apperance | Reddish purple liquid | GB/T 8237.6.1.1 | |
| Viscosity | Pa·s | 0.30~0.50 | RS-V007 |
| thixotropic index | ≥1.5 | RS-V007 | |
| Gel time | min | 15.0~25.0 | GB/T 7193.4.6 |
Note: Gel time measurement at 25°C: resin 50g, curing agent Butanox M-50 1.0g.
| Item | Unit | Measured value | Test Methods |
| Tensile strength | MPa | 65 | GB/T2567-2008 |
| Elongation at break | % | 2.2 | GB/T2567-2008 |
| Bending strength | MPa | 115 | GB/T2567-2008 |
| Bacall hardness | 45 | GB/T3854-2005 | |
| Heat distortion temperature | ℃ | 68 | GB/T1634-2004 |
1:Cast body production method according to GB/T 8237-2005, temperature 25℃, curing system: curing agent Butanox M-50 1.5%;
2: Post-curing treatment of casting body: room temperature×24 hours+60℃×3 hours+80℃×2 hours.
1.The thixotropic agent in the resin will be settled after long term storage, before using, please pour out all the resin in the drum or barrel and stir well before using.
2.When the ambient temperature is high and the gel time of resin is short, the dosage of hardener can not be reduced, and gel delayer should be added as needed.
3.When the construction environment has high humidity or high temperature, it is also easy to cause the surface to be sticky, so you can add the wax liquid appropriately.
The transport should be in accordance with the national "Regulations on the Safe Management of Chemical Dangerous Goods", Chapter V, Transportation and Handling of Chemical Dangerous Goods. The product should be stored in
Cool place under 25℃, avoid fire, isolate heat source and radiation source, shelf life is 3 months under 25℃.
Changzhou JLON Composite Co. is a leading Chinese supplier of various fiberglass and polyester reinforcements for roofing/ceiling/wall/flooring applications. Our main products include the following:
1. Coated glass mat: for ceiling, gypsum board, insulation board (PIR/PUR)
2. Laid scrim: fiberglass, polyester scrim and laminate
3. Fiberglass reinforced aluminum foil
4. Fiberglass nonwoven for roofing, flooring and carpets
5. Polyester nonwoven for waterproofing
JLON is committed to meeting diversified needs of clients. We’re in continuous efforts to improve our supply chain to provide good quality, cost effective products to our clients.
We’re looking forward to building long term business relationship with clients all over the world based on mutual trust.
A: Yes, We usually discuss with customers and help them find solutions.
A: Usually a sample will be prepared within one week after specification agreed.
A: Usually around 2-3 weeks after order confirmed. Exact delivery time depends on order quantity and Off-season/ busy season.
A: Offer TDS of each lot of production for confirmation before delivery.Once you have any quality problem, you can provide samples /pictures and test data. We will give you feedback in short time. If the quality problem confirmed, we will discuss about compensation with you.
A: Usually we do EXW, FOB, CIF and DDU
| Name | Type | 25℃aPa.s Viscosity | 25℃min Gel Time | %Non-volatile | MPa Tensile Strength | %Elongation | MPa Flexural Strength | ℃distortion Temperature | Application&Remarks | Hand lay-up general purpose resin |
| JL-189 | 0.25-0.45 | 10.5-21.5 | 60-66 | 61 | 4.6 | 110 | 62 | Hand lay-up general purpose resin, marine,high damage elongation,water resistance,CCS certification | ||
| JL-191 | 0.25-0.45 | 9.0-17.0 | 61-67 | 64 | 3.6 | 112 | 66 | General hand lay-up,winding,higher elongation | ||
| JL-1032 | 0.34-0.42 | 10.0-30.0 | / | 62 | 2.0 | 118 | 69 | Finshing boat,yacht,hand lay-up, spray up,low shrinkage,water resistance,CCS certification | Hand lay-up,spray up promote thixotropic resin | |
| JL-10070TP | 0.4-0.6 | 10.0-50.0 | / | 58 | 2.0 | 100 | 86 | S/F and F/F double wall tanks,UI1316/1746/1856 certified | ||
| JL-3002 | 0.14-0.18 | 20.0-100.0 | 56.0-62.0 | 270 | / | 300 | / | Vacuum infusion process,RTM process,low viscosity,good fiberglass wettability | Flame retardant resin(data for FRP) | |
| JL-107BH | 0.40-0.50 | 16.0-25.0 | 56.0-62.0 | 300 | / | 325 | / | Good flame retardant property,high mechanical strength,used for ships,vechicles,construction,etc | ||
| JL-T1 | 0.35-0.55 | 7.0-12.0 | 60.0-66.0 | 71 | 3.2 | 110 | 112 | Used for corrosion resistant,high strength pultrusion products,high strength,good heat resistance | Pultrusion resin | |
| JL-611H | 0.50-0.80 | 10.0-18.0 | 64.0-70.0 | 62 | 3.0 | 110 | 60 | General purpose pultrusion resin,high viscosity,good surface gloss | ||
| JL-21 | 0.14-0.18 | 20.0-110.0 | 53.0-59.0 | 60 | 2 | 108 | 65 | Used for fishing boats and yachts,pre-promotion,low reactivity,shrinkage | RTM/Vacuum infusion | |
| JL-25 | 0.14-0.18 | 20.0-110.0 | 53.0-59.0 | 71 | 3.8 | 122 | 75 | Pre-promotion,low heat release,good toughness,CCS certification | ||
| JL-102 | 0.20-0.40 | 7.0-13.0 | 58.0-64.0 | 65 | 2.8 | 120 | 103 | Used for temperature resistance FRP pipe,tank structure layer,corrosion resistance,high thermal deformation temperature | Winding resin | |
| JL-192 | 0.30-0.50 | 18.0-28.0 | 62.0-68.0 | 75 | 3.3 | 120 | 92 | High reactivity,high strength and structural layer | ||
| JL-D31 | 0.30-0.60 | 8.0-16.0 | 58.0-64.0 | 60 | 2.8 | 122 | 90 | Good toughness and strength,suitable for water-resistant gelcoat matrix | Gelcoat matrix resin | |
| JL-D34 | 0.65-1.15 | 8.0-18.0 | 64.0-70.0 | 76 | 2.6 | 128 | 73 | Good toughness and strength,used for toughness general purpose gelcoat matrix | ||
| JL-1017 | 0.50-0.80 | 16.0-24.0 | 62.0-68.0 | 75 | 2.0 | 100 | 70 | Good mechanical properties,good cracking resistance,fast demoulding,used for concrete castling | Casting resin | |
| JL-2250 | 0.13-0.18 | 8.0-14.0 | 66.0-70 | 40 | 1.0 | 60 | 80 | Low shrinkage,low viscosity,high filling rate,used for polyester concrete | ||
| JL-2 | 0.60-0.80 | 8.0-14.0 | 58.5-64.5 | 50 | 1.6 | 83 | 123 | High gloss,water resistance,heat resistance,good electrical properties,SMC/BMC resin | S/BMC molded resin and low shrinkage agent | |
| JL-6 | 1.10-1.50 | 8.0-11.0 | 63.0-69.0 | 62 | 2.4 | 105 | 110 | High reactivity,good thickening,smooth surface,SMC/BMC resin |
JL-1032 is a kind of water resistance resin, viscosity moderation, good mechanical strength. It can be applied in FRP products of motor shell and boats parts as well as lay-up products. It passed CCS approval.
| Item | Unit | Index | Test standard |
| Appearance | -- | Transparent,light yellow | GB/T 8237.4.1.1 |
| Viscosity | 25ºC,Pa.S | 0.25~0.45 | GB/T 7193.1 |
| Gel time | 25ºC,min | 10.5~21.5 | GB/T 7193.6 |
| Acid value | mgKOH/g | 19~27 | GB/T 2895 |
| Non-volatile | % | 59~65 | GB/T 7193.3 |
Gel Time: 50% cyclohexanon peroxide: 4%; Accelerator E1: 4% :
| item | Unit | Measured value | Test standard |
| Barcol Hardness | -- | 46 | GB 3854-83 |
| HDT | ºC | 57 | GB 1634-04 |
| Elongation at break | % | 4.0 | GB/T 2568-95 |
| water absorption | % | 0.1 | GB/T 1462-88 |
Remark : casting matrix should follow GB8237-87
Hardness system : hardener 55%MEKPO :2% ; accelerator E1 :2%
Later Hardness system :60 ºC×2 hours + 80 ºC×2 hours
The loading and transportation must follow the rules in chapter 5 of dangerous chemicals regulations .The products should stored under 25 ºC and avoid the sunshine ,heat source and fire source. The shelf life is 6 month.
JL-10070TP is a medium viscosity orthophthalic unsaturated polyester resin, pre-accelerated, thixotropic, with wax. Extending its FRP products has good mechanical strength and high elongation rate, suitable for general purpose hand lay up FRP products.
JL-10070TP unsaturated polyester resin is a pre-promoted, thixotropic general purpose resin. It has low viscosity, good infiltration to glass fibre, and excellent thixotropic construction.
JL-10070TP unsaturated polyester resin is a pre-promoted, thixotropic general-purpose resin with low viscosity. It is suitable for hand lay-up or injection moulding of various FRP products, such as FRP cooling towers, vehicle shells and other FRP moulded products.
FRP cooling towers, vehicle shells and other FRP moulded products. JL-10070TP contains wax, JL-10070TPN does not contain wax.
| Item | unit | Indicators | Test Methods |
| Apperance | Reddish purple liquid | GB/T 8237.6.1.1 | |
| Viscosity | Pa·s | 0.30~0.50 | RS-V007 |
| thixotropic index | ≥1.5 | RS-V007 | |
| Gel time | min | 15.0~25.0 | GB/T 7193.4.6 |
Note: Gel time measurement at 25°C: resin 50g, curing agent Butanox M-50 1.0g.
| Item | Unit | Measured value | Test Methods |
| Tensile strength | MPa | 65 | GB/T2567-2008 |
| Elongation at break | % | 2.2 | GB/T2567-2008 |
| Bending strength | MPa | 115 | GB/T2567-2008 |
| Bacall hardness | 45 | GB/T3854-2005 | |
| Heat distortion temperature | ℃ | 68 | GB/T1634-2004 |
1:Cast body production method according to GB/T 8237-2005, temperature 25℃, curing system: curing agent Butanox M-50 1.5%;
2: Post-curing treatment of casting body: room temperature×24 hours+60℃×3 hours+80℃×2 hours.
1.The thixotropic agent in the resin will be settled after long term storage, before using, please pour out all the resin in the drum or barrel and stir well before using.
2.When the ambient temperature is high and the gel time of resin is short, the dosage of hardener can not be reduced, and gel delayer should be added as needed.
3.When the construction environment has high humidity or high temperature, it is also easy to cause the surface to be sticky, so you can add the wax liquid appropriately.
The transport should be in accordance with the national "Regulations on the Safe Management of Chemical Dangerous Goods", Chapter V, Transportation and Handling of Chemical Dangerous Goods. The product should be stored in
Cool place under 25℃, avoid fire, isolate heat source and radiation source, shelf life is 3 months under 25℃.
Changzhou JLON Composite Co. is a leading Chinese supplier of various fiberglass and polyester reinforcements for roofing/ceiling/wall/flooring applications. Our main products include the following:
1. Coated glass mat: for ceiling, gypsum board, insulation board (PIR/PUR)
2. Laid scrim: fiberglass, polyester scrim and laminate
3. Fiberglass reinforced aluminum foil
4. Fiberglass nonwoven for roofing, flooring and carpets
5. Polyester nonwoven for waterproofing
JLON is committed to meeting diversified needs of clients. We’re in continuous efforts to improve our supply chain to provide good quality, cost effective products to our clients.
We’re looking forward to building long term business relationship with clients all over the world based on mutual trust.
A: Yes, We usually discuss with customers and help them find solutions.
A: Usually a sample will be prepared within one week after specification agreed.
A: Usually around 2-3 weeks after order confirmed. Exact delivery time depends on order quantity and Off-season/ busy season.
A: Offer TDS of each lot of production for confirmation before delivery.Once you have any quality problem, you can provide samples /pictures and test data. We will give you feedback in short time. If the quality problem confirmed, we will discuss about compensation with you.
A: Usually we do EXW, FOB, CIF and DDU