Unsaturated polyester resins are one of the most commonly used thermosetting resins, and are generally linear polymer compounds with ester and unsaturated double bonds made by polycondensation of unsaturated dibasic acids with diols or saturated dibasic acids with unsaturated diols.
Marine resins, including marine resin for boats,are formulated to be highly water-resistant and are capable of providing a protective barrier against moisture, making them suitable for marine applications.
These resins,including marine resin for wood, exhibit good resistance to saltwater and the corrosive effects of marine environments, ensuring the longevity and durability of boat components.
Marine resins,including marine resin for plaster, have low water absorption properties, which help prevent the resin from deteriorating or weakening when exposed to water.
They form strong bonds with various materials, including fiberglass, ensuring the structural integrity of the boat and its components.
UV Resistance: Marine resins are often UV-resistant, providing protection against the harmful effects of sunlight, which is crucial for the exterior parts of boats.
Low shrinkage during the curing process is a desirable characteristic as it minimizes the risk of voids or delamination in composite boat structures.
JL-191RS unsaturated polyester resin is a kind of general purpose resin, low viscosity, good mechanical strength and high elongation. It can be applied in all kinds of FRP products as well as lay-up products.
item | unit | index | test standard |
Appearance | -- | Clear pale yellow liquid | GB/T 8237.4.1.1 |
viscosity | 25ºC,Pa.S | 0.25~0.45 | GB/T 7193.1 |
gel time | 25ºC,min | 10.5~21.5 | GB/T 7193.6 |
acid value | mgKOH/g | 25~30 | GB/T 2895 |
non-volatile | % | 61~67 | GB/T 7193.3 |
item | unit | measured value | test standard |
Barcol Hardness | -- | 41 | GB 3854-83 |
HDT | ºC | 70 | GB 1634-04 |
Flexural Strength | MPa | 114 | GB/T 2570-95 |
tensile strength | MPa | 60 | GB/T 2568-95 |
Elongation at break | % | 3.5 | GB/T 2568-95 |
Impact Strength | KJ/m2 | 10.2 | GB/T 2571-95 |
Remark: casting matrix should follow GB8237-87
Hardness system: hardener 55%MEKPO:1.5% accelerator E1:1%
60ºC×3 Hours + 80ºC×2 hours
item | unit | measured value | test standard |
Flexural Strength | MPa | 365 | GB/T1449-83 |
tensile strength | MPa | 290 | GB/T1447-83 |
Impact Strength | KJ/m2 | 235 | GB/T 1451-83 |
Remark: FRP according to GB 8237-87
‚Hardness system: hardener55%MEKPO:2% accelerator E1:2% 60ºC×3hours + 110ºC×3 hours
JL-189 resin is an unsaturated polyester resin with benzene tincture, cistincture and standard glycol as the main raw materials. It has been dissolved in styrene cross-linking monomer and has medium viscosity and medium reactivity. It provides good water resistance, processability and mechanical properties. 189 marine unsaturated polyester resin is suitable for hand lay-up process to make FRP boat hull. It is also suitable for cooling tower, pools, sinks, auto parts and storage tanks...
Item | Unit | Specification | Testing Method |
Appearance | -- | Transparent, light yellow liquid | GB/T 8237.4.1.1 |
Viscosity | 25°C,Pa.S | 0.25-0.45 | GB/T 7193.1 |
Gel time | 25°C,min | 10.5-21.5 | GB/T 7193.6 |
Acid value | mgKOH/g | 19-27 | GB/T 2895 |
Solid content | % | 59-65 | GB/T 7193.3 |
Item | Unit | Actual Value | Testing Method |
Barcol hardness | -- | 46 | GB 3854-83 |
Heat distortion temperature | °C | 57 | GB 1634-04 |
Breaking elongation | % | 4.0 | GB/T 2568-95 |
Water absorption | % | 0.1 | GB/T 1462-88 |
Remarks:
1Make casting body according to method in GB 8237-87
2Curing system: curing agent: 55% MEKP: 2% accelerator E1: 2%
3Post curing system: 60°C x 2 hours + 80°C x 2 hours
Item | Unit | Actual Value | Testing Method |
Bending strength | MPa | 298 | GB/T 2570-95 |
Bending flexible modulus | MPa | 1.35 x 104 | GB/T 2570-95 |
Remarks:
1Make FRP according to method in GB 8237-87
2Curing system: curing agent: 55% MEKP: 2% accelerator E1: 2%
3Post curing system: 60°C x 3 hours + 110°C x 2 hours
Marine resin's resistance to water, salt, and UV radiation contributes to the longevity of boats and ensures that they remain in good condition for extended periods.
Marine resins effectively seal the boat's composite components, protecting them from water intrusion, which can lead to rot, delamination, and other structural issues.
These resins,including marine resin for boats,are used not only in boat manufacturing but also in repair work. They allow for effective and lasting repairs to damaged boat parts.
Marine resins provide structural strength to boat components, ensuring their ability to withstand the rigors of the sea.
Manufacturers can customize the formulation of marine resins to meet the specific requirements of different boat types, styles, and sizes.
JL-1032 is a kind of water resistance resin, viscosity moderation, good mechanical strength. It can be applied in FRP products of motor shell and boats parts as well as lay-up products. It passed CCS approval.
Item | Unit | Index | Test standard |
Appearance | -- | Transparent,light yellow | GB/T 8237.4.1.1 |
Viscosity | 25ºC,Pa.S | 0.25~0.45 | GB/T 7193.1 |
Gel time | 25ºC,min | 10.5~21.5 | GB/T 7193.6 |
Acid value | mgKOH/g | 19~27 | GB/T 2895 |
Non-volatile | % | 59~65 | GB/T 7193.3 |
Gel Time: 50% cyclohexanon peroxide: 4%; Accelerator E1: 4% :
item | Unit | Measured value | Test standard |
Barcol Hardness | -- | 46 | GB 3854-83 |
HDT | ºC | 57 | GB 1634-04 |
Elongation at break | % | 4.0 | GB/T 2568-95 |
water absorption | % | 0.1 | GB/T 1462-88 |
Remark : casting matrix should follow GB8237-87
Hardness system : hardener 55%MEKPO :2% ; accelerator E1 :2%
Later Hardness system :60 ºC×2 hours + 80 ºC×2 hours
JL-3002 unsaturated polyester resin is a reactive flame retardant resin, pre-promoted, with low viscosity, good infiltration of glass fibre and high mechanical strength.
The resin has low viscosity, good infiltration of glass fibre, high mechanical strength, etc. It is suitable for the production of large-sized FRP products, such as wind turbine covers and ship hulls, by vacuum infusion or RTM process.
JL-3002-T30 is winter type, suitable for November and February (below 15℃);
JL-3002-T60 is a spring/autumn type, suitable for March-May, September-October (15-25℃);
JL-3002-T90 is the summer type, suitable for June-August (above 25℃).
Item | Unit | JL-3002-T30 | JL-3002-T60 | JL-3002-T90 | Test Methods |
Apperance | Transparent liquid | GB/T 8237.6.1.1 | |||
viscosity | Pa · s | 0.14~0.18 | GB/T 7193.4.1 | ||
*Gel time | min | 20.0~35.0 | 50.0~70.0 | 85.0~100.0 | GB/T 7193.4.6 |
*25°C gel time test: resin 100g, curing agent Butanox M-50 1.5g
Item | Unit | Measured value | Test Methods |
Tensile strength | MPa | 60 | GB/T2567-2008 |
Tensile modulus of elasticity | MPa | 2980 | GB/T2567-2008 |
Elongation at break | % | 3.10 | GB/T2567-2008 |
Bending strength | MPa | 102 | GB/T2567-2008 |
Bending modulus of elasticity | MPa | 3100 | GB/T2567-2008 |
Oxygen index | % | 25 | GB/T2408-2008 |
Heat Distortion Temperature (HDT) | ℃ | 65 | GB/T1634-2004 |
Bacall hardness | 40 | GB/T3854-2005 |
Note:1.Casting method according to GB/T 8237-2005, temperature 25℃, curing system: curing agent Butanox M-50 1.5%;
2.Post-curing treatment of casting body: room temperature x 24 hours + 60℃ x 3 hours + 80℃ x 2 hours.
The loading and transportation must follow the rules in chapter 5 of dangerous chemicals regulations. The products should store under 25 ºC and avoid the sunshine ,heat source and fire source. The shelf life is 6 months.
Changzhou JLON Composite Co. is a leading Chinese supplier of various fiberglass and polyester reinforcements for roofing/ceiling/wall/flooring applications. Our main products include the following:
1. Coated glass mat: for ceiling, gypsum board, insulation board (PIR/PUR)
2. Laid scrim: fiberglass, polyester scrim and laminate
3. Fiberglass reinforced aluminum foil
4. Fiberglass nonwoven for roofing, flooring and carpets
5. Polyester nonwoven for waterproofing
JLON is committed to meeting diversified needs of clients. We’re in continuous efforts to improve our supply chain to provide good quality, cost effective products to our clients.
We’re looking forward to building long term business relationship with clients all over the world based on mutual trust.
A: Yes, We usually discuss with customers and help them find solutions.
A: Usually a sample will be prepared within one week after specification agreed.
A: Usually around 2-3 weeks after order confirmed. Exact delivery time depends on order quantity and Off-season/ busy season.
A: Offer TDS of each lot of production for confirmation before delivery.Once you have any quality problem, you can provide samples /pictures and test data. We will give you feedback in short time. If the quality problem confirmed, we will discuss about compensation with you.
A: Usually we do EXW, FOB, CIF and DDU
Unsaturated polyester resins are one of the most commonly used thermosetting resins, and are generally linear polymer compounds with ester and unsaturated double bonds made by polycondensation of unsaturated dibasic acids with diols or saturated dibasic acids with unsaturated diols.
Marine resins, including marine resin for boats,are formulated to be highly water-resistant and are capable of providing a protective barrier against moisture, making them suitable for marine applications.
These resins,including marine resin for wood, exhibit good resistance to saltwater and the corrosive effects of marine environments, ensuring the longevity and durability of boat components.
Marine resins,including marine resin for plaster, have low water absorption properties, which help prevent the resin from deteriorating or weakening when exposed to water.
They form strong bonds with various materials, including fiberglass, ensuring the structural integrity of the boat and its components.
UV Resistance: Marine resins are often UV-resistant, providing protection against the harmful effects of sunlight, which is crucial for the exterior parts of boats.
Low shrinkage during the curing process is a desirable characteristic as it minimizes the risk of voids or delamination in composite boat structures.
JL-191RS unsaturated polyester resin is a kind of general purpose resin, low viscosity, good mechanical strength and high elongation. It can be applied in all kinds of FRP products as well as lay-up products.
item | unit | index | test standard |
Appearance | -- | Clear pale yellow liquid | GB/T 8237.4.1.1 |
viscosity | 25ºC,Pa.S | 0.25~0.45 | GB/T 7193.1 |
gel time | 25ºC,min | 10.5~21.5 | GB/T 7193.6 |
acid value | mgKOH/g | 25~30 | GB/T 2895 |
non-volatile | % | 61~67 | GB/T 7193.3 |
item | unit | measured value | test standard |
Barcol Hardness | -- | 41 | GB 3854-83 |
HDT | ºC | 70 | GB 1634-04 |
Flexural Strength | MPa | 114 | GB/T 2570-95 |
tensile strength | MPa | 60 | GB/T 2568-95 |
Elongation at break | % | 3.5 | GB/T 2568-95 |
Impact Strength | KJ/m2 | 10.2 | GB/T 2571-95 |
Remark: casting matrix should follow GB8237-87
Hardness system: hardener 55%MEKPO:1.5% accelerator E1:1%
60ºC×3 Hours + 80ºC×2 hours
item | unit | measured value | test standard |
Flexural Strength | MPa | 365 | GB/T1449-83 |
tensile strength | MPa | 290 | GB/T1447-83 |
Impact Strength | KJ/m2 | 235 | GB/T 1451-83 |
Remark: FRP according to GB 8237-87
‚Hardness system: hardener55%MEKPO:2% accelerator E1:2% 60ºC×3hours + 110ºC×3 hours
JL-189 resin is an unsaturated polyester resin with benzene tincture, cistincture and standard glycol as the main raw materials. It has been dissolved in styrene cross-linking monomer and has medium viscosity and medium reactivity. It provides good water resistance, processability and mechanical properties. 189 marine unsaturated polyester resin is suitable for hand lay-up process to make FRP boat hull. It is also suitable for cooling tower, pools, sinks, auto parts and storage tanks...
Item | Unit | Specification | Testing Method |
Appearance | -- | Transparent, light yellow liquid | GB/T 8237.4.1.1 |
Viscosity | 25°C,Pa.S | 0.25-0.45 | GB/T 7193.1 |
Gel time | 25°C,min | 10.5-21.5 | GB/T 7193.6 |
Acid value | mgKOH/g | 19-27 | GB/T 2895 |
Solid content | % | 59-65 | GB/T 7193.3 |
Item | Unit | Actual Value | Testing Method |
Barcol hardness | -- | 46 | GB 3854-83 |
Heat distortion temperature | °C | 57 | GB 1634-04 |
Breaking elongation | % | 4.0 | GB/T 2568-95 |
Water absorption | % | 0.1 | GB/T 1462-88 |
Remarks:
1Make casting body according to method in GB 8237-87
2Curing system: curing agent: 55% MEKP: 2% accelerator E1: 2%
3Post curing system: 60°C x 2 hours + 80°C x 2 hours
Item | Unit | Actual Value | Testing Method |
Bending strength | MPa | 298 | GB/T 2570-95 |
Bending flexible modulus | MPa | 1.35 x 104 | GB/T 2570-95 |
Remarks:
1Make FRP according to method in GB 8237-87
2Curing system: curing agent: 55% MEKP: 2% accelerator E1: 2%
3Post curing system: 60°C x 3 hours + 110°C x 2 hours
Marine resin's resistance to water, salt, and UV radiation contributes to the longevity of boats and ensures that they remain in good condition for extended periods.
Marine resins effectively seal the boat's composite components, protecting them from water intrusion, which can lead to rot, delamination, and other structural issues.
These resins,including marine resin for boats,are used not only in boat manufacturing but also in repair work. They allow for effective and lasting repairs to damaged boat parts.
Marine resins provide structural strength to boat components, ensuring their ability to withstand the rigors of the sea.
Manufacturers can customize the formulation of marine resins to meet the specific requirements of different boat types, styles, and sizes.
JL-1032 is a kind of water resistance resin, viscosity moderation, good mechanical strength. It can be applied in FRP products of motor shell and boats parts as well as lay-up products. It passed CCS approval.
Item | Unit | Index | Test standard |
Appearance | -- | Transparent,light yellow | GB/T 8237.4.1.1 |
Viscosity | 25ºC,Pa.S | 0.25~0.45 | GB/T 7193.1 |
Gel time | 25ºC,min | 10.5~21.5 | GB/T 7193.6 |
Acid value | mgKOH/g | 19~27 | GB/T 2895 |
Non-volatile | % | 59~65 | GB/T 7193.3 |
Gel Time: 50% cyclohexanon peroxide: 4%; Accelerator E1: 4% :
item | Unit | Measured value | Test standard |
Barcol Hardness | -- | 46 | GB 3854-83 |
HDT | ºC | 57 | GB 1634-04 |
Elongation at break | % | 4.0 | GB/T 2568-95 |
water absorption | % | 0.1 | GB/T 1462-88 |
Remark : casting matrix should follow GB8237-87
Hardness system : hardener 55%MEKPO :2% ; accelerator E1 :2%
Later Hardness system :60 ºC×2 hours + 80 ºC×2 hours
JL-3002 unsaturated polyester resin is a reactive flame retardant resin, pre-promoted, with low viscosity, good infiltration of glass fibre and high mechanical strength.
The resin has low viscosity, good infiltration of glass fibre, high mechanical strength, etc. It is suitable for the production of large-sized FRP products, such as wind turbine covers and ship hulls, by vacuum infusion or RTM process.
JL-3002-T30 is winter type, suitable for November and February (below 15℃);
JL-3002-T60 is a spring/autumn type, suitable for March-May, September-October (15-25℃);
JL-3002-T90 is the summer type, suitable for June-August (above 25℃).
Item | Unit | JL-3002-T30 | JL-3002-T60 | JL-3002-T90 | Test Methods |
Apperance | Transparent liquid | GB/T 8237.6.1.1 | |||
viscosity | Pa · s | 0.14~0.18 | GB/T 7193.4.1 | ||
*Gel time | min | 20.0~35.0 | 50.0~70.0 | 85.0~100.0 | GB/T 7193.4.6 |
*25°C gel time test: resin 100g, curing agent Butanox M-50 1.5g
Item | Unit | Measured value | Test Methods |
Tensile strength | MPa | 60 | GB/T2567-2008 |
Tensile modulus of elasticity | MPa | 2980 | GB/T2567-2008 |
Elongation at break | % | 3.10 | GB/T2567-2008 |
Bending strength | MPa | 102 | GB/T2567-2008 |
Bending modulus of elasticity | MPa | 3100 | GB/T2567-2008 |
Oxygen index | % | 25 | GB/T2408-2008 |
Heat Distortion Temperature (HDT) | ℃ | 65 | GB/T1634-2004 |
Bacall hardness | 40 | GB/T3854-2005 |
Note:1.Casting method according to GB/T 8237-2005, temperature 25℃, curing system: curing agent Butanox M-50 1.5%;
2.Post-curing treatment of casting body: room temperature x 24 hours + 60℃ x 3 hours + 80℃ x 2 hours.
The loading and transportation must follow the rules in chapter 5 of dangerous chemicals regulations. The products should store under 25 ºC and avoid the sunshine ,heat source and fire source. The shelf life is 6 months.
Changzhou JLON Composite Co. is a leading Chinese supplier of various fiberglass and polyester reinforcements for roofing/ceiling/wall/flooring applications. Our main products include the following:
1. Coated glass mat: for ceiling, gypsum board, insulation board (PIR/PUR)
2. Laid scrim: fiberglass, polyester scrim and laminate
3. Fiberglass reinforced aluminum foil
4. Fiberglass nonwoven for roofing, flooring and carpets
5. Polyester nonwoven for waterproofing
JLON is committed to meeting diversified needs of clients. We’re in continuous efforts to improve our supply chain to provide good quality, cost effective products to our clients.
We’re looking forward to building long term business relationship with clients all over the world based on mutual trust.
A: Yes, We usually discuss with customers and help them find solutions.
A: Usually a sample will be prepared within one week after specification agreed.
A: Usually around 2-3 weeks after order confirmed. Exact delivery time depends on order quantity and Off-season/ busy season.
A: Offer TDS of each lot of production for confirmation before delivery.Once you have any quality problem, you can provide samples /pictures and test data. We will give you feedback in short time. If the quality problem confirmed, we will discuss about compensation with you.
A: Usually we do EXW, FOB, CIF and DDU